· Chemical Analysis
Name | MgO | CaO | Fe2O3 | SiO2 | Al2O3 |
---|---|---|---|---|---|
Value | ≥96 | ≤1.0 | ≤0.5 | ≤2.0 | ≤0.5 |
· Physical Analysis
Flow Rate(F.R) | Tap Density | ||||||
---|---|---|---|---|---|---|---|
120±10 S/100g | 2.27-2.35 g/cm³ | ||||||
Sieve Analysis (%) | |||||||
Sieve size(mesh) | +40 | +60 | +80 | +140 | +200 | +325 | -325 |
Sieve size(mm) | 0.425 | 0.25 | 0.18 | 0.106 | 0.075 | 0.045 | -0.045 |
Value | ≤0.5 | 25±5 | 25±5 | 25±5 | 15±5 | 10±5 | ≤5 |
· Electrical Property
Sample Electrical heating elements
Materials: SUS 304 tube
Rolling: 8.0mm→6.6mm
Length: 780mm
Spiral:Ni80Cr20,∅0.3mm
Heating time: 15min
· Packing
25KG in a plastic bag with a carton or a woven bag.Special Packing is available on requirement.
· Remarks
①MEG-1 is high temperature powder.
②This kind of powder is treated without silicone oil or treated with pretty light silicone oil.Electrical Grade Magnesium Oxide is non-toxic, but with some dust Anti-dust respirator andgloves are proposed to use during operation.
③This kind of powder is treated without silicone oil or treated with pretty light silicone oil.Electrical Grade Magnesium Oxide is non-toxic, but with some dust Anti-dust respirator andgloves are proposed to use during operation.
④Mainly used in air heating elements with wattage loading less than 10w/c㎡.
⑤The elements can stand 1050℃±50℃ annealing for 15-30minutes and requires immediate sealing.
⑥Electrical Grade Magnesium Oxide should be stored in dry places, and are suggested to be usedout within 6 months after delivery.