· Chemical Analysis
Name | MgO | CaO | Fe2O3 | SiO2 | Al2O3 |
---|---|---|---|---|---|
Value | ≥95 | ≤1.5 | ≤0.6 | ≤0.5 | ≤0.5 |
· Physical Analysis
Flow Rate(F.R) | Tap Density | ||||||
---|---|---|---|---|---|---|---|
160±20 S/100g | 2.28-2.35 g/cm³ | ||||||
Sieve Analysis (%) | |||||||
Sieve size(mesh) | +40 | +60 | +80 | +140 | +200 | +325 | -325 |
Sieve size(mm) | 0.425 | 0.25 | 0.18 | 0.106 | 0.075 | 0.045 | -0.045 |
Value | ≤0.5 | 30±5 | 20±5 | 20±5 | 10±5 | 10±5 | 6±2 |
· Electrical Property
Sample Electrical heating elements
Materials: SUS 304 tube
Rolling: ∅8.0mm→6.6mm
Length: 420mm
Spiral: Ni80Cr20,∅0.3mm
Heating time: 15min
· Packing
25KG in a plastic bag with a carton or a woven bag .Special packing is available on requirement.
· Remarks
①MEZ-TM1 is medium-high temperature powder.
②This kind of powder is treated with heavy silicone oil.
③Electrica Grade Magnesium Oxide is non-toxic, but with some dust.Anti-dust respirator and gloves are proposedto use during operation.
④Mainly used in the elements of copper tube with wattage loading less than 8w/c㎡.
⑤Elements stuffed with this material are proposed to be annealed at420℃ for 15minutes, and don’t require sealing.
⑥Electrical Grade Magnesium Oxide should be stored in dry places, and are suggested to be used out within 6 months after delivery.